Long Lasting Industrial Anticorrosion Floor Coating Providing Superior Resistance To Corrosion And Mechanical Damage
Product Introduction
Epoxy anti-corrosive glass flake floor paint is a high-performance heavy-duty anti-corrosive coating, specially designed for harsh corrosive environments such as industrial floors, sewage pools, and storage tanks.
Application Scope
Epoxy anti-corrosive glass flake floor paint is applied to anti-corrosive and waterproof areas in workshops of electroplating, chemical, food, pharmaceutical, printing and dyeing, hardware, machinery, and other industries.
Performance Characteristics
The performance characteristic for Epoxy anti-corrosive glass flake floor paint is as follows:
1.Resistant to corrosion by chemicals such as acids, alkalis, and salts.
2.Impact-resistant, heavy-load resistant, good tensile strength, and excellent overall performance.
3.Aesthetic and durable; also has dust-proof, anti-cracking, and waterproof properties.
Construction Process
1.Base surface treatment.
2.Brush the sealing primer.
3.Pave the glass fiber cloth.
4.Roll and brush the anti-corrosive intermediate coat (Steps 3 and 4 can be repeated according to requirements).
5.Grind and clean the dust.
6.Roll and brush the anti-corrosive topcoat.
Technical Indicators
Item | Parameter | Test Standard |
Mixing Ratio | Component A : Component B = 25 : 3 (weight ratio) | - |
Drying Time (25℃) | Tack-free time ≤2h, full cure time ≤24h | GB/T 1728 |
Theoretical Spreading Rate | 3.3-3.7㎡/kg | - |
Acid and Alkali Resistance | No abnormality after 30 days of immersion in 10% H₂SO₄/NaOH | GB/T 1763 |
Pot Life (25℃) | 3-8 hours (depending on curing agent type) | - |
Technical specifications
| Property | Value |
|---|---|
| Mixing Ratio | Component A : Component B = 25 : 3 (weight ratio) |
| Drying Time (25℃) | Tack-free time ≤2h, full cure time ≤24h · GB/T 1728 |
| Theoretical Spreading Rate | 3.3-3.7 ㎡ /kg |
| Acid and Alkali Resistance | No abnormality after 30 days of immersion in 10% H₂SO₄/NaOH · GB/T 1763 |
| Pot Life (25℃) | 3-8 hours (depending on curing agent type) |